JHL-2015S is a modified epoxy stone compound rubber, designed for the production of high-strength composite board. Excellent anti-aging properties can be used for white marble composite, fiberglass back mesh.
Product Features：
◆ moderate viscosity, good operation.
◆ excellent anti-yellowing performance.
◆ curing hard work after aging resistance.
◆ with a greater impact on the ambient temperature, the construction temperature should be maintained at 20 degrees or more, 25 hours 6 hours 12 hours can be dismantled into the next process.
The main technical and performance parameters:
project | Typical values | |
Exterior | A | Beige easy flow of liquid |
B | Beige easy flow of liquid | |
Viscosity | A | 10000~15000 |
B | 2000~4000 | |
Mixing ratio A: B | 2∶1 | |
100 g cup gel time | 20min~35min | |
25 ℃ curing time table dry / hard work | 1.5~2.5h/12~15h | |
Solid content | ≥95 | |
Product use method:
◆ open the AB plastic drums, should be first with a special stirrer will A agent, B agent were stirring (A, B stirrer can not be mixed, otherwise the glue is easy to respond to agglomeration resulting in hollowing), to avoid long-term storage lead to a small amount of layered adhesive Results.
◆ Sizing should be kept dry, there is no obvious water stains on the stone surface, dust and oil, pay special attention to the water inside the cave to deal with clean, should try to be bound to dry and keep the sticky surface above 25 ℃.
◆ A component and B component in accordance with the A: B = 2: 1 deployment is used to cash, in 20min to complete.
◆ glue and other means to remove the clamp after touching dry. Polishing, to be such a layer of hard work.
Product use Note:
◆ This series of special glue, applies only to white marble series of high-strength composite plate, the applicable period (that is, operating time) significantly affected by temperature, high temperature is the application period is short.
◆ Sizing should be completely according to the ratio of A: B = 2: 1 deployment to ensure the best bonding effect, otherwise it will affect the bonding strength.
◆ AB plastic drums open, you should first use a special stirrer will A agent, B agent were stirring. If not stirred evenly, may cause the plate surface appears light red to brown red water stains, rubber layer appears brown red and degumming and so on.
◆ B glue should be fully mixed after mixing, the product after curing the surface shiny, such as glue layer after curing the surface of filamentous or massive color, indicating A, B glue mixing is not sufficient.
◆ time should not be too much time to adjust the plastic, glue the number of more likely to be due to fast response and slightly shortened the pot life. To 25 ℃ when the amount of 20 minutes is appropriate, the deployment of a good plastic should be used once
◆ The workshop should be well ventilated. This product may stimulate the skin of some people, when the glue should do a good job of labor protection, glue splashed on the skin should be immediately rubbed with acetone or advanced hand sanitizer, then rinse with water, when splashed into the eyes, the application of large amounts of water Rinse and seek immediate medical attention.
◆ Although this product can be composite panel and substrate in the case of high temperature as usual compound, but should still try to keep the adhesive surface dry, such as dry lines have been built, can still be short-term drying, and other stone and Substrate surface drying and then compound, will be able to get a better bonding effect.
◆ When the ambient temperature is too low, the glue will thicken and slow down the curing speed, can be heated by A glue on the stone to warm or improve the temperature of the construction environment to make glue thinning, and thus speed up the curing speed. It is worth noting that: The ideal curing temperature of the composite rubber is 25 ℃ ~ 75 ℃; when the temperature is too low in winter, as far as possible heating curing (such as a drying line has been built for a short time baking, or gas gun And so on the stone surface for a short time baking), will be able to get a better curing effect, otherwise there may be a low intensity of the situation.
◆ The components of the product should be sealed and stored in a cool warehouse, to avoid direct sunlight, the opening of the A plastic and B plastic Do not cover the wrong lid.
Packaging, transportation and storage:
1, packaging 25KG iron or plastic packaging specifications.
2, the transport process should be rain, sun, to prevent damage to the packaging, moisture.
3, stored in a cool dry place, away from fire, strong acid, alkali and strong oxidants.
4, in accordance with the provisions of the transport and storage conditions, from the date of production from the storage period of 12 months.
5, JHL-2015S for non-dangerous goods, according to the general merchandise disposal.
6, the color is gradually deepening during storage is a normal phenomenon, does not affect the use of results. After opening the use of packaging barrels should be tightly closed lid, to avoid long-term exposure to air.
Special Note:
The Company of the above data and text description are from sincerity, but I do not know whether it is suitable for your company's construction technology and use. Therefore, please use this product before the samples from the Company to obtain the test, if you have any questions, please feel free to contact the Company.